Tetracalcium phosphate 1.67 Ca10(PO4)6(OH)2 Hydroxyapatite Table 1 Various calcium phosphates[4] Ca/P Formula Name 2.0 Ca4O(PO4)2 Tetracalcium phosphate 1.67 Ca10(PO4)6(OH)2 Hydroxyapatite Ca10-xH2x (PO4)6(OH)2 Amorphous calcium phosphate 1.50 Ca3(PO4)2 Tricalcium phosphate 1.33 Ca8H2(PO4)6 5H2O Oktacalsium phosphate 1.0 CaHPO4 Dicalsium phosphate CaHPO4.2H2O Dicalsium phosphate dehydrate Ca2P2O7 calsium pyrophosphate 0.7 Ca7(P5O16)2 Heptacalsium Phosphate 0.67 Ca4H2P6O20 Tetracalsium dihydrogen phosphate 0.5 Ca(H2PO4)2.H2O Monocalsium phosphate monohydrate Ca(PO3)2 Calciummetaphosphate
Calcium Phosphate Chemical structure close to bone mineral Osteoconductive Biocompatible Bioresorbable HA and TCP Closely resemble the mineral phase of bone Bioactive material HA is very stable crystalline material TCP is biodegradable and bioresorbable material
Penambal Gigi Komposit penambal gigi terdiri dari resin dan serbuk yang mengandung kalsium Apatit (komponen utama gigi) Komposit yang digunakan di Indonesia masih import Calcium hydroxide (Rp 450.000) 15 gram Tricalcium phosphate ($84.99) 2 gram Calcium hydroxide (Rp 590.000) 15 gram Zink oxide ($66.89) 10 gram
Pengembangan Biomaterial Bagian Biofisika Departemen Fisika IPB Hasilnya Mengembangkan sintesis apatit berbasis bahan alami dan sintetik Hidroksiapatit (HAp) Biphasic Calcium Phosphate (BCP) Menggunakan cangkang telur Komposit Penambal Gigi Resin Untuk mengetahui kemampuan adaptasi komposit yang dihasilkan dilakukan uji in vitro.
Sintesis Sintesis HAp Sintesis BCP Larutan (NH4)2HPO4 + Suspensi senyawa kalsium dari cangkang telur Pereaksian dengan metode presipitasi pada T=37oC Presipitat disintering pada T=900oC selama 5 jam Sintesis BCP Larutan (NH4)2HPO4 + Suspensi senyawa kalsium dari cangkang telur Pereaksian dengan metode hidrotermal pada T=300oC Selama 8 jam Hasil disintering pada T=1000oC selama 5 jam